| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||
| 基本性能 | 24小時吸水率 | ASTM D-570 | 0.5 | % | ||
| 物理性能 | 熔體流動速率 | ASTM D-1238 | 18 | g/10min | ||
| 泰伯磨耗量 | CS-17輪 | ASTM D-1044 | 7 | mg/1000rev | ||
| 泰伯磨耗量 | H 18輪 | ASTM D-1044 | 70 | mg/1000rev | ||
| 比重 | ASTM D-792 | 1.20 | ||||
| 機械性能 | 埃佐沖擊強度 | 23℃ | ASTM D-256 | 不破裂 | J/m | |
| 斷裂拉伸力 | ASTM D-638 | 40 | MPa | |||
| 初耐撕裂性能 | ASTM D-1004 | 158 | kn/m | |||
| 撓曲模量 | 23℃ | ASTM D-790 | 207 | MPa | ||
| 斷裂伸長 | ASTM D-638 | 500 | % | |||
| 拉伸力 | 5%伸長 | ASTM D-638 | 6.9 | MPa | ||
| 10%伸長 | ASTM D-638 | 10.3 | MPa | |||
| 硬度計硬度 | ASTM D-2240 | 55 | ||||
| 熱性能 | 維卡軟化點 | ASTM D-1525 | 180 | ℃ | ||
| 熱畸變溫度 | @0.5MPa | ASTM D-648 | 90 | ℃ | ||
| 熱畸變溫度 | @0.18MPa | ASTM D-648 | 49 | ℃ | ||
| 熔點 | ASTM D-3418 | 203 | 熔點 | |||
| 其它性能 | 耐揉曲切口增長性能 | ASTM D-1052 | >5×105 | |||
美國杜邦Hytrel? 5526
THERMOPLASTIC POLYESTER ELASTOMER
美國杜邦Hytrel? 5526產品說明:
55 Shore D High Performance High Flow Polyester Elastomer Developed for Injection Molding
添加劑 |
|
特性 |
|
RoHS 合規性 |
|
形式 |
|
加工方法 | 熱成型注射成型 |
多點數據 | Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (TPE) (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Shear Stress vs. Shear Rate (ISO 11403-1)Specific Volume vs Temperature (ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2) |
部件標識代碼 (ISO 11469) |
|
樹脂ID (ISO 1043) |
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
密度 | 1.19 | g/cm3 | ISO 1183 |
熔流率（熔體流動速率） | 18 | g/10 min | ISO 1133 |
溶化體積流率（MVR） (220°C/2.16 kg) | 1.07 | in3/10min | ISO 1133 |
收縮率 | ISO 294-4 | ||
橫向流量 | 1.4 | % | |
流量 | 1.4 | % | |
吸水率 | ISO 62 | ||
73°F, 24 hr | 0.60 | % | |
飽和, 73°F, 0.0787 in | 0.60 | % | |
平衡, 73°F, 0.0787 in, 50% RH | 0.20 | % | |
| 硬度 | 額定值 | 單位制 | 測試方法 |
肖氏硬度 | ISO 868 | ||
邵氏 D | 55 | ||
邵氏 D, 15 秒 | 51 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 | 27600 | psi | ISO 527-2 |
拉伸應力 | ISO 527-2 |
要了解更多關于美國杜邦 TPE 5526的相關資料報告，請聯系我們